Anti-sintering ZrO2-modified Ni/α-Al2O3 catalyst for CO methanation

Qing Liu, Fangna Gu*, Ziyi Zhong, Guangwen Xu, Fabing Su

*Corresponding author for this work

Research output: Contribution to journalArticlepeer-review

18 Scopus citations

Abstract

To obviously reduce the sintering behavior of Ni particles in Ni/α-Al2O3 catalysts during CO methanation reaction, ZrO2 was deposited onto the Ni/α-Al2O3 catalyst surface by a modified impregnation method. It was observed that the ZrO2-modified catalyst with an appropriate amount of ZrO2 showed enhanced catalytic activity due to the increased H2 uptake and Ni dispersion. During the 103h-lifetime test, the ZrO2-modified catalyst exhibited higher stability and anti-sintering performance than the unmodified one, because the partial coverage of ZrO2 particles could effectively prevent Ni particles from sintering during the reaction at high temperatures. The findings obtained in this study should be conducive to the design and development of supported metal catalysts for high temperature reactions with enhanced stability.

Original languageEnglish
Pages (from-to)20979-20986
Number of pages8
JournalRSC Advances
Volume6
Issue number25
DOIs
StatePublished - 2016
Externally publishedYes

Fingerprint Dive into the research topics of 'Anti-sintering ZrO<sub>2</sub>-modified Ni/α-Al<sub>2</sub>O<sub>3</sub> catalyst for CO methanation'. Together they form a unique fingerprint.

Cite this