Band offsets and Fermi level pinning at metal-Al₂O₃ interfaces

TY - JOUR

T1 - Band offsets and Fermi level pinning at metal-Al2O3 interfaces

AU - Kornblum, Lior

AU - Rothschild, Jonathan A.

AU - Kauffmann, Yaron

AU - Brener, Reuven

AU - Eizenberg, Moshe

PY - 2011/10/18

Y1 - 2011/10/18

N2 - Disparities between the predicted and the measured effective work functions (EWFs) in advanced metal oxide semiconductor devices, or Fermi-level pinning (FLP), have gained significant attention when high-k dielectrics began to emerge. Using a systematic approach for EWF extraction, combined with a comparison to unpinned SiO2 references, it was found that no intrinsic FLP exists in the model dielectric Al2O3. Extrinsic FLP was found with one of the metals investigated Ta, where a 0.4 eV increase in the EWF was observed in the electrical characteristics and confirmed by backside spectroscopy. The physical origins of the band offsets related to the EWF increase have been analyzed in detail. A 2-nm interfacial layer at the Ta-Al2O3 interface has been found and is suggested as the source of extrinsic FLP. Interfacial dipoles originating from Ta-O chemical bonds are considered as the mechanism responsible for the band offset. The results of this model system are then used to explain some of the peculiarities occurring at complex devices which are used in technological applications.

AB - Disparities between the predicted and the measured effective work functions (EWFs) in advanced metal oxide semiconductor devices, or Fermi-level pinning (FLP), have gained significant attention when high-k dielectrics began to emerge. Using a systematic approach for EWF extraction, combined with a comparison to unpinned SiO2 references, it was found that no intrinsic FLP exists in the model dielectric Al2O3. Extrinsic FLP was found with one of the metals investigated Ta, where a 0.4 eV increase in the EWF was observed in the electrical characteristics and confirmed by backside spectroscopy. The physical origins of the band offsets related to the EWF increase have been analyzed in detail. A 2-nm interfacial layer at the Ta-Al2O3 interface has been found and is suggested as the source of extrinsic FLP. Interfacial dipoles originating from Ta-O chemical bonds are considered as the mechanism responsible for the band offset. The results of this model system are then used to explain some of the peculiarities occurring at complex devices which are used in technological applications.

UR - http://www.scopus.com/inward/record.url?scp=80455178810&partnerID=8YFLogxK

U2 - 10.1103/PhysRevB.84.155317

DO - 10.1103/PhysRevB.84.155317