Study of porous silica based films as low-k dielectric material and their interface with copper metallization

Ilanit Fisher*, Wayne D. Kaplan, Moshe Eizenberg, Michael Nault, Timothy Weidman

*Corresponding author for this work

Research output: Contribution to journalConference articlepeer-review

4 Scopus citations

Abstract

The success of future gigascale integrated circuits (IC) chip technology depends critically upon the reduction of the interconnects RC delay time. This calls for the development of new low dielectric constant (low-k) insulators, and for work on their integration with lower resistivity copper metallization. A porous silica based film prepared by surfactant templated self-assembly spin-on deposition (SOD) is an attractive candidate as a low-k material. In this research we have studied the structure, chemical composition and bonding of the film and its interface with copper metallization. The decomposition and vaporization of the surfactant in the last step of film deposition resulted in a film with an amorphous structure, as determined by XRD and TEM analysis. Its high porosity (35-58%) was confirmed by XRR and RBS measurements. XPS analysis of the Si2p transition indicated three types of bonding: Si-O, O-Si-C and Si-C. The bonding characteristics were also investigated by FTIR analysis. The effect of a hydrogen plasma post-treatment process on the film topography and bonding was determined by AFM and XPS, respectively. It was found that direct H2 plasma exposure significantly affected the surface roughness of the film and type of chemical bonding. The structure and properties of various PECVD deposited capping layers were also studied, as was the interface between the porous dielectric and Ta, TaxN and Cu (PVD deposited films) after annealing at 200-700°C in vacuum environment for 30 min. At temperatures up to 500°C, no significant diffusion of Cu or Ta into the porous film was detected, as determined by RBS. No copper penetration was detected up to 700°C, according to AES and SIMS analysis. However, at 700°C copper dewetting occurred when it was deposited directly on the porous silica based film.

Original languageEnglish
Pages (from-to)355-361
Number of pages7
JournalMaterials Research Society Symposium Proceedings
Volume716
DOIs
StatePublished - 2002
Externally publishedYes
EventSilicon Materials - Processing, Characterization and Reliability - San Francisco, CA, United States